A novel polymer thin films was fabricated by anchoring polymer from reaction solution (monomer, Alcohol and hydrochloric acid). The thickness of the film increases with concentration of monomer and acid, and it decreases at large concentrations of acid. The surface roughness of films were increased with thickness. Mean diameter of polymer particles in thin films were about 280.4,180.7and 135.3 nm For returned film, mean diameter of polymer particles were about 81.5 nm and it was less roughness. In EIS, the ohmic resistance of film 180±23 at thickness=110 nm and 13710±2170 Ohm at thickness = 907 nm.
Al-Hamdan, Ahmad; Al-Falah, Ahmad; and Al-Deri, Fawaz
"Fabrication and Study Thin Films from PFPy by Anchoration,"
International Journal of Thin Film Science and Technology: Vol. 10
, Article 6.
Available at: https://digitalcommons.aaru.edu.jo/ijtfst/vol10/iss2/6